AA Alclad 6061 Alüminyum alaşım
Veri güncellemeleri
Bu malzemenin 127 özelliği vardır - burada yalnızca bir alt kümesi gösterilmektedir.
Sıcaklıklar ve koşullar genelinde ayrıntılı değerler de dahil olmak üzere tam malzeme özelliklerinin kilidini açın.
Ücretsiz kayıt gereklidir • Anında erişim
AA Alclad 6061 Fiziksel özellikler
Sıcaklık
Bu malzemenin 127 özelliği vardır - burada yalnızca bir alt kümesi gösterilmektedir.
Sıcaklık ve koşullar genelinde ayrıntılı fiziksel özellik değerlerinin kilidini açın.
Ücretsiz kayıt gereklidir • Anında erişim
AA Alclad 6061 Isıl İşlem
- The times and temperatures are typical for various forms, sizes and methods of manufacture and may not exactly describe the optimum treatment for a specific item.
The nominal temperatures at which metal is heated (applies both for solution and precipitation heat treatment) should be attained as rapidly as possible and maintained ± 5°C of nominal during the time at temperature.
The time at precipitation heat treatment temperature will depend on time required for load to reach temperature. The times shown are based on rapid heating, with soaking time measured from the time the load reached within 5°C of the applicable temperature.
Material should be quenched from the solution heat-treating temperature as rapidly as possible and with minimum delay after removal from the furnace. Quenching is typically performed by immersion of wrought products in a cold water bath, although some forgings are quenched in hot-water. Quenching may be performed by alternative means such as total immersion in an aqueous polymer solution, liquefied gas, hot water, or boiling water, or by air blast or fog to minimize distortion provided samples from the material. The use of high-velocity high-volume jets of cold water is also effective for some materials.
For sheet
Temper T4: Solution heat treated at 530°C, quenched, naturally aged.
Temper T42: Solution heat treated at 530°C, quenched, naturally aged.
Temper T6: Solution heat treated at 530°C, quenched, precipitation heat treated at 160°C for 18 hours.
Temper T62: Solution heat treated at 530°C, quenched, precipitation heat treated at 160°C for 18 hours.
For plate
Temper T4 (applies only to tread plate): Solution heat treated at 530°C, quenched, naturally aged.
Temper T451: Solution heat treated at 530°C, quenched, naturally aged. Stress-relieved by stretching is required to produce a specified amount of permanent set subsequent to solution heat treatment.
Temper T42: Solution heat treated at 530°C, quenched, naturally aged.
Temper T6 (applies only to tread plate): Solution heat treated at 530°C, quenched, precipitation heat treated at 160°C for 18 hours.
Temper T651: Solution heat treated at 530°C, quenched, precipitation heat treated at 160°C for 18 hours. Stress-relieved by stretching is required to produce a specified amount of permanent set prior to any precipitation heat treatment.
Temper T62: Solution heat treated at 530°C, quenched, precipitation heat treated at 160°C for 18 hours.
AA Alclad 6061 Mekanik özellikler
Sıcaklık
Doğru seçimi yapmak için eksiksiz mekanik özelliklere mi ihtiyacınız var?
Mukavemet, sertlik, yorulma ve daha fazlası hakkında eksiksiz verilere ulaşın.
Ücretsiz kayıt gereklidir • Anında erişim
AA Alclad 6061 Uluslararası eşdeğer malzemeler
3 sonuçtan 3 tanesi gösteriliyor.
Eşdeğerlik kategorileri, kimyasal bileşim ve mekanik özellik karşılaştırmalarını gösterir — uygulamanız için geçerli şartnameye göre uygunluğunu her zaman doğrulayın.
3 uluslararası eşdeğerin tam listesine mi ihtiyacınız var?
Standart, üretici ve eşdeğerlik kategorisine göre ayrıntılı eşleştirmeler ile tüm 3 eşdeğer kaliteleri görün.
Ücretsiz kayıt gereklidir • Anında erişim
Uygulamanız için en uygun olan malzeme seçiminizi optimize edin - Demo Rezervasyonu Yapın
- 3Çapraz Referanslar
- -Bileşim
- 48Mekanik Özellikler
- 30Fiziksel Özellikler
- 1Isıl İşlem
- -Metalografi
- -İşlenebilirlik
- 13Gerilme-Gerinim
- -Şekillendirilebilirlik
- 1Yorulma
- -Kırılma
- 14Sürünmek
- 14Bağlantılar
- -Kaplamalar
- -Boyutlar
- -Triboloji
- 3Korozyon
- -Yaşlanma
- -Hava şartlarına dayanıklılık
- -Radyasyon etkisi
- -Toplam Tedarikçiler