MIL 17-7PH Stainless steels
Data updates
This material has 51 properties — only a subset is shown here.
Unlock full material properties, including detailed values across temperatures and conditions.
Free registration required • Instant access
MIL 17-7PH Physical Properties
Temperature
This material has 51 properties — only a subset is shown here.
Unlock detailed physical values across temperatures and conditions.
Free registration required • Instant access
MIL 17-7PH Heat Treatments
- Solution treatment: at 1950°F; Cold worked material (condition C) shall be heat-treated to spring temper (condition CH 900) by age-tempering at 900°F for 60 minutes to 90 minutes; For Sheet and Strip, hold 3 minutes plus 1 minute for each 0.01 Inch thickness; Medium for quenching: water, polymer or air. Air quench may be applied to materials up to 0.500 Inch thick. Water quenching is recommended for materials over 0.500 inch thick; Austenitized (T): at 1400°F, hold 90 min. (+15min/-0 min), quenched in air to room temperature. Transformation treatment at 60°F min. hold 30 min.; Austenitized (R): at 1750°F, hold 10 min. +15min/-0 min, quenched in air to room temperature. Transformation treatment at -100°F, min. hold 480 min.
MIL 17-7PH Mechanical Properties
Temperature
Need complete mechanical properties to make the right choice?
Get complete data on strength, hardness, fatigue, and more.
Free registration required • Instant access
MIL 17-7PH International Equivalent Materials
Showing 11 of 12 results.
Equivalence categories reflect chemical-composition and mechanical-property comparison — always verify suitability against the governing specification for your application.
Need the full list of 12 international equivalents?
See all 12 equivalent grades with detailed mapping by standard, producer and equivalence category.
Free registration required • Instant access
Optimize material selection for your application - Book A Demo
- 12Cross References
- -Composition
- 26Mechanical Properties
- 3Physical Properties
- 1Heat Treatment
- -Metallography
- -Machinability
- -Stress-Strain
- -Formability
- -Fatigue
- -Fracture
- -Creep
- -Joints
- -Coatings
- -Dimensions
- -Tribology
- -Corrosion
- -Ageing
- -Weatherability
- -Irradiation
- 9Total Suppliers