PROPRIETARY UGI 4418 AIR 不锈钢
材料组别:
黑色金属 / 不锈钢
国家与地区/标准:
PROPRIETARY
数据更新
最新更新: 2021-06
更新总数: 2
更新历史
2021-04
PROPRIETARY UGI 4418 AIR 化学成分
化学元素
数值
单位
CAS 编号
化学元素
C
数值
≤ 0.060
单位
%
CAS 编号
7440-44-0
化学元素
Cr
数值
15.0 – 17.0
单位
%
CAS 编号
7440-47-3
化学元素
Cu
数值
≤ 0.5
单位
%
CAS 编号
7440-50-8
Ugitech SA, Product Data Sheets,
需要完整的材料性能数据吗？
查看完整材料数据 ›
需要注册 • 立即访问
需要注册 • 立即访问
PROPRIETARY UGI 4418 AIR 物理性能
温度
PROPRIETARY UGI 4418 AIR 热处理
- Forging: heating between 1150°C and 1200°C is recommended. Forging must preferably be carried out at a temperature of between 1200°C and 900°C, followed by air cooling;
Softening: soft annealing is carried out between 600 and 650°C;
Quenching: quenching heat treatment consists of austenitizing between 1010°C and 1060°C, followed by oil quenching (or air quenching for smaller sections). To limit the risks of quenching cracks, tempering must be carried out as soon as possible after the quenching operation, after returning to the ambient temperature;
Tempering: QT 900 level: tempering between 550°C and 620°C;
QT 1100 and QT1150 levels: tempering between 375°C and 405°C;
The tempering period is generally between 2 h and 4 h and is followed by air or oil cooling. Double tempering can be used to soften the grade further. The temperature range between 400°C and 450°C should be avoided, as it can lead to excessive metal embrittlement.
PROPRIETARY UGI 4418 AIR 机械性能
PROPRIETARY UGI 4418 AIR 的全球近似对照材料
显示 15 条结果，共计 83 条。
材料牌号
标准
国家与地区 / 生产商
近似类型
近似对照材料反映了不同材料间化学成分的相似性和力学性能的相似性——请务必根据具体应用场景的适用标准和条件具体核实材料的适用性。
根据您的应用场景优化材料选择 - 预约演示
- 83交叉引用
- 10化学成分
- 47机械性能
- 17物理性能
- 1热处理
- 1金相组织
- -切削加工性能
- 10应力-应变
- -成形性能
- -疲劳
- -断裂
- -爬行
- -焊接接头
- -涂层
- -尺寸
- -摩擦学
- -腐蚀
- -老化
- -耐候性
- -辐照
- 74供应商总数