PROPRIETARY ExELL HOT-DIE 工具钢
材料组别:
黑色金属 / 工具钢
国家与地区/标准:
PROPRIETARY
数据更新
最新更新: 2018-07
更新总数: 2
更新历史
2018-06
PROPRIETARY ExELL HOT-DIE 化学成分
化学元素
数值
单位
CAS 编号
Ellwood Specialty Steel, Product Data Sheets,
需要完整的材料性能数据吗？
查看完整材料数据 ›
需要注册 • 立即访问
需要注册 • 立即访问
PROPRIETARY ExELL HOT-DIE 物理性能
PROPRIETARY ExELL HOT-DIE 热处理
- Stress relieving: After rough machining of an annealed part, heat slowly to 1200°F (649°C), equalize and hold 1-2 hours. Furnace cool to 900°F (482°C) and then air cool to room temperature.
Annealing: With a protective atmosphere or vacuum furnace, heat slowly to 1560°F (849°C). Equalize and hold 1 hour per inch of thickness. Furnace cool 20°F (11°C)/hr to 1100°F (593°C) and equalize. Cool freely in air to room temperature. Hardness will be 217 max HB.
Preheating: Heat to 1200°F (649°C) and equalize. Continue heating to 1550°F (843°C) and equalize. Complete heating to hardening temperature.
Hardening: Typical austentizing range is 1875-1900°F (1024-1038°C). A hardening temperature of 1885°F (1029°C) is normally used for most applications. Hold at hardening temperature 30 minutes.
Quenching: Should be performed as rapidly as possible (50°F (10°C)/min) without promoting excess movement or cracking. Typical quenching media include: High speed gas with sufficient positive pressure and circulation in a vacuum furnace; Warm oil flash quench; Martempering bath or fluidized bed at 575-1020°F (302-1868°C), then air cool. Temper as soon as part reaches 120-150°F (49-66°C).
Tempering: Temper immediately after quenching to about 150°F (66°C). Temper a minimum of two times (three preferred) with intermediate cooling to room temperature. Do not temper in the range of 800-975°F (427-524°C) to avoid temper embrittleness.
PROPRIETARY ExELL HOT-DIE 机械性能
根据您的应用场景优化材料选择 - 预约演示
- -交叉引用
- 6化学成分
- 21机械性能
- 12物理性能
- 1热处理
- -金相组织
- -切削加工性能
- 3应力-应变
- -成形性能
- -疲劳
- -断裂
- -爬行
- -焊接接头
- -涂层
- -尺寸
- -摩擦学
- -腐蚀
- -老化
- -耐候性
- -辐照
- 1供应商总数