PROPRIETARY 20MnV6 结构钢
材料组别:
黑色金属 / 结构钢
国家与地区/标准:
PROPRIETARY
参考价格:
数据更新
最新更新: 2018-02
更新总数: 2
更新历史
2016-07
PROPRIETARY 20MnV6 化学成分
化学元素
数值
单位
CAS 编号
化学元素
C
数值
0.1600 – 0.2200
单位
%
CAS 编号
7440-44-0
化学元素
Mn
数值
1.3000 – 1.6000
单位
%
CAS 编号
7439-96-5
化学元素
P
数值
≤ 0.0300
单位
%
CAS 编号
7723-14-0
Interlloy Pty. Ltd., Product Data Sheets,
需要完整的材料性能数据吗？
查看完整材料数据 ›
需要注册 • 立即访问
需要注册 • 立即访问
PROPRIETARY 20MnV6 物理性能
PROPRIETARY 20MnV6 热处理
- Water quenched at 925°C and tempered at 580°C. Carbonitriding: Heat to 870 - 880°C in a gaseous media consisting of carbon monoxide/hydrocarbon plus ammonia, hold for sufficient time to develop the required case depth, carbon and nitrogen content, followed by quenching in oil or water as required. Tempering immediately while still hand warm at 150 - 200°C will reduce stresses and improve the toughness of the case. Carburizing: Pack, salt or gas carburize at 880 - 920°C, holding for sufficient time to develop the required case depth and carbon content, followed by a suitable heat treatment cycle to optimise case and/or core properties. Case Hardening: Water quench from 760 - 780°C. Core Refining: Oil quench from 870 - 880°C prior to water quench as above. Tempering immediately following water quench at 150 - 200°C will reduce stresses and improve toughness of case. High or Medium Frequency Induction Hardening: Heat to the austenitic temperature range 870 - 925°C, and required case depth, quench immediately in oil or water as required. Tempering immediately at 150 - 200°C will reduce stress and improve the toughness of the case. Nitriding: Carried out at 490 - 530°C followed by slow cooling (no quench) reducing the problem of distortion. If pre-hardened and tempered feedstock is used always ensure that the tempering temperature employed is at least 15°C above the nitriding temperature. Hardening: Heat to 870 - 925°C as required, hold until the temperature is uniform throughout the section, soak 10 - 15 min/ 25mm of section and quench in oil or water as required.Temper immediately while still hand warm. Tempering: Reheat to 500 - 600°C as required, hold until temperature is uniform throughout the section, soak for 1 h/ 25mm of section. Cool in still air. Normalizing: Heat to 900 - 925°C, hold until temperature is uniform throughout the section, soak for 30 minutes and cool in still air. Stress Relieving Following Welding: Heat the weld area to 550 - 650°C, soak for 30 minutes and cool in still air or furnace.
PROPRIETARY 20MnV6 机械性能
温度
PROPRIETARY 20MnV6 国际等效材料
显示 15 / 154 条结果。
材料牌号
标准
国家与地区 / 生产商
近似类型
等效类别反映化学成分和机械性能的比较 — 请始终根据适用于您应用的相关规范验证适用性。
根据您的应用场景优化材料选择 - 预约演示
- 154交叉引用
- 6化学成分
- 24机械性能
- 3物理性能
- 1热处理
- -金相组织
- -切削加工性能
- -应力-应变
- -成形性能
- -疲劳
- -断裂
- -爬行
- -焊接接头
- -涂层
- -尺寸
- -摩擦学
- -腐蚀
- -老化
- -耐候性
- -辐照
- 136供应商总数