MSZ C15R 结构钢
材料组别:
黑色金属 / 结构钢
国家与地区/标准:
匈牙利 / MSZ
参考价格:
数据更新
最新更新: 2024-12
更新总数: 5
更新历史
2020-12
2018-10
2018-08
2017-08
MSZ C15R 化学成分
化学元素
数值
单位
CAS 编号
EN 10084: 2008 / 表面硬化钢 - 交货技术条件
需要完整的材料性能数据吗？
查看完整材料数据 ›
需要注册 • 立即访问
需要注册 • 立即访问
MSZ C15R 物理性能
温度
MSZ C15R 热处理
- Carburizing at 880-980°C (The carburizing temperature depends on the chemical composition of the steel, the mass of the product and the carburizing medium. If the steels are direct hardened, in general, a temperature of 950°C is not exceeded. For special procedures, for example under vacuum, higher temperatures (for example 1020-1050°C) are not unusual);
Direct and simple hardening at 830-870°C (The kind of quenching agent depends on, for example the shape of the products, the cooling conditions and the amount of furnace filling. If the steels are direct hardened and if there is a danger of distortion, they should be quenched from a temperature between the core-hardening and case-hardening temperatures);
Double hardening: Core-hardening at 880-920°C and Case-hardening at 780-820°C;
Tempering at 150-200°C (Time for tempering as a guide: 1h minimum). - 渗碳：880 - 980°C；注意：如果钢是直接硬化的，通常渗碳温度不超过 950°C。对于特殊工艺，如在真空下，更高的温度（如 1020 - 1050°C）并不罕见。芯部硬化：880 - 920°C；表面硬化：780 - 820°C；回火：150 - 200°C（作为指导，最少 1 小时）。
MSZ C15R 机械性能
MSZ C15R 国际等效材料
显示 15 / 217 条结果。
材料牌号
标准
国家与地区 / 生产商
近似类型
等效类别反映化学成分和机械性能的比较 — 请始终根据适用于您应用的相关规范验证适用性。
根据您的应用场景优化材料选择 - 预约演示
- 217交叉引用
- 42化学成分
- 101机械性能
- 16物理性能
- 3热处理
- -金相组织
- -切削加工性能
- 15应力-应变
- -成形性能
- -疲劳
- -断裂
- -爬行
- 83焊接接头
- -涂层
- 8尺寸
- 1摩擦学
- 8491腐蚀
- -老化
- -耐候性
- -辐照
- 160供应商总数