PROPRIETARY BÖHLER W300 工具钢
材料组别:
黑色金属 / 工具钢
国家与地区/标准:
PROPRIETARY
数据更新
最新更新: 2021-04
更新总数: 1
更新历史
PROPRIETARY BÖHLER W300 化学成分
化学元素
数值
单位
CAS 编号
Böhler Edelstahl, Product Data Sheets,
需要完整的材料性能数据吗？
查看完整材料数据 ›
需要注册 • 立即访问
需要注册 • 立即访问
PROPRIETARY BÖHLER W300 物理性能
温度
PROPRIETARY BÖHLER W300 热处理
- Annealing: 750 to 800°C / Controlled slow cooling in furnace (10 to 20°C/h) to approx. 600°C air cooling.
Stress relieving: 600 to 650°C, slow cooling in furnace. Slow cooling in furnace; intended to relieve stresses set up by extensive machining, or in complex shapes. After through heating, hold in neutral atmosphere for 1 to 2 hours.
Hardening: 1000 to 1040°C, oil, salt bath (500 to 550°C), air. Holding time after temperature equalization: 15 to 30 minutes.
Tempering: Slow heating to tempering temperature immediately after hardening/time in furnace: 1 hour for every 20 mm of work piece thickness, but not less than 2 hours/ air cooling (minimum holding time: 1 hour);
1st tempering approx. 30°C above maximum secondary hardness
2nd tempering to desired working hardness
3rd tempering for stress relieving. 30 - 50°C below highest tempering temperature
PROPRIETARY BÖHLER W300 机械性能
PROPRIETARY BÖHLER W300 国际等效材料
显示 15 / 108 条结果。
材料牌号
标准
国家与地区 / 生产商
近似类型
等效类别反映化学成分和机械性能的比较 — 请始终根据适用于您应用的相关规范验证适用性。
根据您的应用场景优化材料选择 - 预约演示
- 108交叉引用
- 6化学成分
- 7机械性能
- 32物理性能
- 4热处理
- -金相组织
- -切削加工性能
- -应力-应变
- -成形性能
- -疲劳
- -断裂
- -爬行
- -焊接接头
- -涂层
- -尺寸
- -摩擦学
- -腐蚀
- -老化
- -耐候性
- -辐照
- 93供应商总数