PROPRIETARY Hiperco 50A 磁性和电气材料
材料组别:
黑色金属 / 磁性和电气材料
国家与地区/标准:
PROPRIETARY
数据更新
最新更新: 2021-07
更新总数: 2
更新历史
2016-02
PROPRIETARY Hiperco 50A 化学成分
化学元素
数值
单位
CAS 编号
Carpenter Technology Corporation, Product Data Sheets,
需要完整的材料性能数据吗？
查看完整材料数据 ›
需要注册 • 立即访问
需要注册 • 立即访问
PROPRIETARY Hiperco 50A 物理性能
温度
PROPRIETARY Hiperco 50A 热处理
- A dry hydrogen atmosphere or high vacuum is recommended to minimize oxide contamination during annealing. When hydrogen is employed and the inside retort temperature is above 482°C (900°F), the entry dew point should be dryer than -51°C (-60°F) and the exit dew point should be dryer than about -40°C (-40°F).
Anneal parts at 857-871°C (1575-1600°F) for 4 hours in dry hydrogen or vacuum and cool at 139-222°C/h (250-400°F)/h until 316°C (600°F) is reached, after which any cooling rate can be employed.
Lower temperature heat treating can be utilized to achieve higher strength in Hiperco 50A at the expense of magnetic properties.
Annealed laminations can be heat-treated in an oxygen bearing atmosphere in the range of 300-500°C (600-900°F) to grow a thin oxide layer on the surfaces. This coating serves to provide an enhanced level of electrical insulation between laminations, greatly reducing eddy current effects during AC excitation. Oxide heat treatment soak times are generally less than 5 hours and can be adjusted to refine coating thickness.
PROPRIETARY Hiperco 50A 机械性能
PROPRIETARY Hiperco 50A 的全球近似对照材料
显示 3 条结果，共计 4 条。
材料牌号
标准
国家与地区 / 生产商
近似类型
近似对照材料反映了不同材料间化学成分的相似性和力学性能的相似性——请务必根据具体应用场景的适用标准和条件具体核实材料的适用性。
根据您的应用场景优化材料选择 - 预约演示
- 4交叉引用
- 5化学成分
- 6机械性能
- 16物理性能
- 1热处理
- -金相组织
- -切削加工性能
- 2应力-应变
- -成形性能
- -疲劳
- -断裂
- -爬行
- -焊接接头
- -涂层
- -尺寸
- -摩擦学
- -腐蚀
- -老化
- -耐候性
- -辐照
- 4供应商总数