ASME SA-553 Type I 结构钢
材料组别:
黑色金属 / 结构钢
国家与地区/标准:
美国 / ASME
数据更新
最新更新: 2024-02
更新总数: 5
更新历史
2024-01
2023-11
2023-10
2019-11
ASME SA-553 Type I 化学成分
化学元素
数值
单位
CAS 编号
ASME Boiler and Pressure Vessel Code An International Code Section II - Part A Ferrous Material Specifications, American Society of Mechanical Engineers, 2025
需要完整的材料性能数据吗？
查看完整材料数据 ›
需要注册 • 立即访问
需要注册 • 立即访问
ASME SA-553 Type I 物理性能
温度
ASME SA-553 Type I 热处理
- All plates shall be heat treated by heating to a suitable temperature within the range of 800 to 925°C (1475 to 1700°F), holding for a sufficient time to obtain uniform temperature throughout the plate thickness and then quenching in water. Subsequently the plates shall be tempered within the range from 565 to 635°C (1050 to 1175°F), holding at this temperature for a minimum of 1,2 min/mm of thickness but not less than 15 min, and cool in air or water quench at a rate not less than 167°C/h (300°F/h).
Prior to the tempering treatment, the plates may be subjected to an intermediate heat treatment consisting of heating to a temperature in the range from 630 to 700°C (1165 to 1290°F); holding at that temperature for a suitable time, but in no case less than 15 min, and then water-quenching to below 150°C (300°F) in the case of plate thicknesses of more than 16 mm or cooling in air or water-quenching to below 150°C (300°F) in the case of plate thicknesses of 16 mm and under.
ASME SA-553 Type I 机械性能
ASME SA-553 Type I 国际等效材料
显示 15 / 161 条结果。
材料牌号
标准
国家与地区 / 生产商
近似类型
等效类别反映化学成分和机械性能的比较 — 请始终根据适用于您应用的相关规范验证适用性。
根据您的应用场景优化材料选择 - 预约演示
- 161交叉引用
- 6化学成分
- 13机械性能
- 59物理性能
- 1热处理
- -金相组织
- -切削加工性能
- -应力-应变
- -成形性能
- -疲劳
- -断裂
- 24爬行
- -焊接接头
- -涂层
- 34尺寸
- -摩擦学
- -腐蚀
- -老化
- -耐候性
- -辐照
- 129供应商总数