X20Cr13 (欧盟 / EN) 材料性能
其他名称:
材料组别:
黑色金属 / 不锈钢
国家与地区/标准:
欧盟 / EN
数据更新
最新更新: 2025-03
更新总数: 14
更新历史:
2024-12
2024-03
2021-10
2020-03
2019-09
2019-06
2018-04
2017-08
2017-01
2016-11
2015-02
2015-01
2014-04
机械性能
温度
物理性能
温度
化学成分
化学元素
数值
单位
CAS 编号
EN 10088-1: 2023 / 不锈钢 - 第 1 部分: 不锈钢的清单
热处理
- Hot formed at 1100-800°C, slow cooled.<br>A: annealed at 750-850°C.<br>QT700: quenched at 950-1050°C, oil or air cooled. Tempered at 650-750°C.<br>QT800: quenched at 950-1050°C, oil or air cooled. Tempered at 600-700°C.
- Hot forming: 1100-800°C, slow cooling; Annealing (+A): 745-825°C, air cooling; Quenching (+QT700): 950-1050°C, oil or air cooling; (If heat treatment is carried out in a continuous furnace, the upper part of the range specified should usually be preferred, or even exceeded); Tempering: 650-750°C; Quenching (+QT800): 950-1050°C, oil or air cooling; (If heat treatment is carried out in a continuous furnace, the upper part of the range specified should usually be preferred, or even exceeded); Tempering: 600-700°C.