PROPRIETARY WM H-26 Aceros para herramientas

Grupo de materiales: Aleaciones Ferrosas / Aceros para herramientas
País/Estándar: PROPRIETARY

Actualizaciones de datos

Última actualización: 2018-06
Número total de actualizaciones: 1
Historial de actualizaciones

Este material cuenta con 24 propiedades — aquí solo se muestra una parte.

Accede a todas las propiedades del material, incluyendo valores detallados según temperatura y condiciones.

Ver datos completos del material ›
Se requiere registro gratuito • Acceso inmediato

Se requiere registro gratuito • Acceso inmediato

PROPRIETARY WM H-26 Composición química

Criterios
Valor
Unidad
Número CAS
Criterios
C
Valor
0.57
Unidad
%
Número CAS
7440-44-0
Criterios
Cr
Valor
4.00
Unidad
%
Número CAS
7440-47-3
Criterios
V
Valor
1.00
Unidad
%
Número CAS
7440-62-2
Criterios
W
Valor
val1
Datos completos disponibles con acceso gratuito Ver datos completos del material
Unidad
%
Número CAS
7440-33-7

Ellwood Specialty Steel, Product Data Sheets,

¿Buscas datos completos de desempeño de materiales?

Ver datos completos del material ›
Se requiere registro gratuito • Acceso inmediato

Se requiere registro gratuito • Acceso inmediato

PROPRIETARY WM H-26 Propiedades físicas

Temperatura

Propiedad/Valor
Módulo de elasticidad
190 — 210 GPa
Desbloquea todos los detalles
Datos completos disponibles con acceso gratuito Ver datos completos del material
Densidad
7.72 — 8 kg/dm³
Desbloquea todos los detalles
Datos completos disponibles con acceso gratuito Ver datos completos del material
Coeficiente de Poisson
0.27 — 0.3
Desbloquea todos los detalles
Datos completos disponibles con acceso gratuito Ver datos completos del material

Este material cuenta con 24 propiedades — aquí solo se muestra una parte.

Consulta propiedades físicas detalladas en distintas temperaturas y condiciones.

Ver datos completos del material ›
Se requiere registro gratuito • Acceso inmediato

Se requiere registro gratuito • Acceso inmediato

PROPRIETARY WM H-26 Tratamiento Térmico

  • During forging and annealing, the standard precautions applicable to all high speed steels should be followed. Like all 8 to 9% molybdenum high speed steels, it is subject to considerable decarburization during any heating cycle.
    Salt baths or controlled atmosphere furnaces are preferable for hardening. Danger of decarburization or carburization is eliminated in properly operated salt baths, while in controlled atmosphere furnaces any partial decarburization or carburization which may result is usually so slight as to be of no consequences on tools which are to be ground after hardening.
    Like other high speed steels, should not be held at the quenching temperature but should be removed form the furnace as soon as uniformly heated. Quenching in oil is preferred, although will attain maximum hardness when cooled in air or in a hot bath at about 100°F (38°C).
    For hot work applications with the 60% carbon grade, a wider hardening range is permissible depending upon the application. Normally, a temperature of 2100-2150°F (1149-1177°C) will be employed. For higher hot hardness and wear resistance, the temperature should be raised, and for higher toughness it should be lowered. The lower carbon can be quenched, in air, oil or hot salt bath. Usually oil quenching is recommended.

PROPRIETARY WM H-26 Propiedades mecánicas

Temperatura

Propiedad/Valor
Dureza de Rockwell (HR)
33 — 63
Desbloquea todos los detalles
Datos completos disponibles con acceso gratuito Ver datos completos del material
Tamaño de grano
val1
Datos completos disponibles con acceso gratuito Ver datos completos del material
Desbloquea todos los detalles
Datos completos disponibles con acceso gratuito Ver datos completos del material

¿Buscas información completa sobre propiedades mecánicas para tomar la mejor decisión?

Obtén información completa sobre resistencia, dureza, fatiga y más.

Ver datos completos del material ›
Se requiere registro gratuito • Acceso inmediato

Se requiere registro gratuito • Acceso inmediato

Reservar una demo

Optimiza la selección de materiales para tu aplicación - Reservar una demo

  • -Referencias cruzadas
  • 4Composición
  • 15Propiedades mecánicas
  • 3Propiedades físicas
  • 1Tratamiento térmico
  • -Metalografía
  • -Maquinabilidad
  • -Esfuerzo-Deformación
  • -Conformabilidad
  • -Fatiga
  • -Fractura
  • -Bicho raro
  • -Uniones
  • -Revestimientos
  • -Dimensiones
  • -Tribología
  • -Corrosión
  • -Envejecimiento
  • -Resistencia a la intemperie
  • -Irradiación
  • 1Proveedores Totales