PROPRIETARY Ferrium M54 Aceros estructurales y de construcción

Grupo de materiales: Aleaciones Ferrosas / Aceros estructurales y de construcción

País/Estándar: PROPRIETARY

Actualizaciones de datos

Última actualización: 2025-06

Número total de actualizaciones: 2

Historial de actualizaciones

2016-01

Este material cuenta con 53 propiedades — aquí solo se muestra una parte.

Accede a todas las propiedades del material, incluyendo valores detallados según temperatura y condiciones.

PROPRIETARY Ferrium M54 Composición química

Criterios

Valor

Unidad

Número CAS

Criterios

Valor

0.3000

Unidad

Número CAS

7440-44-0

Criterios

Valor

7.0000

Unidad

Número CAS

7440-48-4

Criterios

Valor

1.0000

Unidad

Número CAS

7440-47-3

Criterios

Valor

val1

Unidad

Número CAS

7439-98-7

Criterios

Valor

val1

Unidad

Número CAS

7440-02-0

Criterios

Valor

val1

Unidad

Número CAS

7440-62-2

Criterios

Valor

val1

Unidad

Número CAS

7440-33-7

QuesTek Innovations LLC, Product Data Sheet,

¿Buscas datos completos de desempeño de materiales?

PROPRIETARY Ferrium M54 Propiedades físicas

Temperatura

0 - 30°C 30 - 100°C 100 - 300°C ≥ 300°C

Propiedad/Valor

Módulo de elasticidad

190 — 210 GPa

Desbloquea todos los detalles

La conductividad térmica

26.322 W/(m∙°C)

Desbloquea todos los detalles

Densidad

val1 kg/dm³

Desbloquea todos los detalles

Capacidad calorífica

val1 J/(kg∙°C)

Desbloquea todos los detalles

Coeficiente de Poisson

val1

Desbloquea todos los detalles

Módulo de corte

val1 GPa

Desbloquea todos los detalles

Este material cuenta con 53 propiedades — aquí solo se muestra una parte.

Consulta propiedades físicas detalladas en distintas temperaturas y condiciones.

PROPRIETARY Ferrium M54 Tratamiento Térmico

Normalizing: 1074°C (1965°F) for 1 hour and air cool.
Annealing: Can be softened by subcritical annealing by heating to 799°C (1470°F) ± 14°C (25°F), holding for 60 minutes, + 60 minutes, and then air cool to room temperature, followed by annealing by heating to 652°C (1205°F) ± 28°C (50°F) for no less than 8 hours, and then air cool to room temperature.
Solution Treatment: 1060°C (1940°F) 1 hour and oil quench or equivalent.
Quenching: Gas, Oil, or Equivalent.
Cold Treatment: Following solution treatment, -73°C (-100°F) for 1 hour and air warm.
Straightening: Operations such as shaft straightening (if required) should preferably be done after the sub zero treatment but prior to the temper. This metal fully mechanical strength after tempering, and thus trying to straighten parts after tempering will be more difficult. If excessive distortion exists after the solution treatment, quench and sub-zero treatment, then it is recommended to heat the part to 200°C (392°F) in air for 1 hour, hot-straighten the part (temperature determined by amount of force required to straighten part; temperature should be maintained below 371°C (700°F) to avoid any tempering or decarburization; a small oxide layer may form at this temperature), and allow the component to air cool. The full temper cycle must then be applied.
Stress Relieving: If it is desired to stress-relieve a machined part in the mill-annealed condition as a means to help prevent distortion during further processing (e.g. if significant forces were imposed on the part during machining), then either of two options are recommended: I. Produce the part in a rough-machined state with adequate stock material on all surfaces so that oxide scale can be removed, and then stress-relieve the part at ~649°C (1200°F) for 2 hours, followed by cooling in air. Then complete all final machining operations. II. Produce the part in a fully- or nearly-fully-machined state prior to solution treatment, sub-zero treatment quench and temper, and then stress-relieve the part at 371°C (700°F) for 2 hours or 274°C (525°F) for 4 hours, followed by cooling in air.
Tempering: Temper at 516°C (960°F) for 8 to 12 hours and air cool.

PROPRIETARY Ferrium M54 Propiedades mecánicas

Temperatura

0 - 30°C

Propiedad/Valor

Resistencia a la Tracción

≥ 2020 MPa

Desbloquea todos los detalles

Alargamiento, A

≥ 15 %

Desbloquea todos los detalles

Reducción de área

val1 %

Desbloquea todos los detalles

Dureza de Rockwell (HR)

val1

Desbloquea todos los detalles

Límite elástico, Rp0.2

≥ 1724 MPa

Desbloquea todos los detalles

¿Buscas información completa sobre propiedades mecánicas para tomar la mejor decisión?

Obtén información completa sobre resistencia, dureza, fatiga y más.

PROPRIETARY Ferrium M54 Materiales equivalentes internacionales

Mostrando 1 de 2 resultados.

Material

Estándar

País / Productor

Categoría de Equivalencia

Material

K91973

Estándar

UNS

País / Productor

Estados Unidos

Categoría de Equivalencia

Oficial

Las categorías de equivalencia reflejan la comparación de composición química y propiedades mecánicas — verifique siempre la idoneidad según la especificación aplicable a su aplicación.

¿Necesita la lista completa de 2 equivalentes internacionales?

Consulte los 2 grados equivalentes con mapeo detallado por norma, productor y categoría de equivalencia.

Optimiza la selección de materiales para tu aplicación - Reservar una demo

¿Buscas comparar materiales y tomar mejores decisiones?

Accede a datos confiables de materiales, compara opciones y decide con mayor rapidez.

Con Total Materia, puedes:

Comparar materiales basándote en datos reales de ingeniería

Encontrar materiales equivalentes entre distintas normas

Evaluar el desempeño según tus condiciones específicas

Verificar el cumplimiento con normativas internacionales

Descubre cómo funciona para tu aplicación específica

Iniciar visita guiada

2Referencias cruzadas

15Composición
8Propiedades mecánicas
23Propiedades físicas
1Tratamiento térmico
-Metalografía
-Maquinabilidad

2Esfuerzo-Deformación
-Conformabilidad
-Fatiga
-Fractura
-Bicho raro

-Uniones
-Revestimientos
-Dimensiones
-Tribología

-Corrosión
-Envejecimiento
-Resistencia a la intemperie
-Irradiación

2Proveedores Totales