GB QTANi30Si5Cr5 Cast irons

Material group: Ferrous Alloys / Cast irons

Country / Standard: China / GB

Data updates

Latest Update: 2026-05

Total number of updates: 3

Update History

2015-09 2014-08

This material has 4462 properties — only a subset is shown here.

Unlock full material properties, including detailed values across temperatures and conditions.

GB QTANi30Si5Cr5 Chemical Composition

CRITERIA

VALUE

UNIT

CAS NUMBER

CRITERIA

VALUE

≤ 2.6

UNIT

CAS NUMBER

7440-44-0

CRITERIA

VALUE

4.5 – 5.5

UNIT

CAS NUMBER

7440-47-3

CRITERIA

VALUE

≤ 0.5

UNIT

CAS NUMBER

7440-50-8

CRITERIA

VALUE

val1

UNIT

CAS NUMBER

7439-96-5

CRITERIA

VALUE

val1

UNIT

CAS NUMBER

7440-02-0

CRITERIA

VALUE

val1

UNIT

CAS NUMBER

7723-14-0

CRITERIA

VALUE

val1

UNIT

CAS NUMBER

7704-34-9

CRITERIA

VALUE

val1

UNIT

CAS NUMBER

7440-21-3

GB/T 26648: 2026 / Austenitic iron castings

Looking for full material performance data?

GB QTANi30Si5Cr5 Physical Properties

Temperature

0 - 30°C 100 - 300°C

PROPERTY / VALUE

Modulus of Elasticity

90 GPa

Unlock full details

Thermal Conductivity

12.6 W/(m∙°C)

Unlock full details

Density

7.45 kg/dm³

Unlock full details

Heat Capacity

val1 J/(kg∙°C)

Unlock full details

Service Temperature

val1 °C

Unlock full details

Coefficient of Thermal Expansion (CTE)

val1 10^-6/°C

Unlock full details

This material has 4462 properties — only a subset is shown here.

Unlock detailed physical values across temperatures and conditions.

GB QTANi30Si5Cr5 Heat Treatments

Stress-relief heat-treatment procedure

The stress-relief heat-treatment procedure is as follows:
a) heating rate not greater than 150°C/h; heat to 625-650°C and hold for 2 h;
b) for each additional 25 mm of section thickness, increase the holding time by 1 h;
c) cooling rate not greater than 100°C/h; furnace-cool to 200°C, then remove from the furnace and air-cool.

High-temperature stabilization heat-treatment procedure

For workpieces intended for service at temperatures above 500°C, high-temperature stabilization heat treatment shall be carried out. The recommended high-temperature stabilization heat-treatment procedure for castings is as follows:
a) heating rate not greater than 150°C/h; heat to 955-1040°C and hold for 3-5 h;
b) for each additional 25 mm of section thickness, increase the holding time by 1 h;
c) after the specified holding time has been reached, remove from the furnace and air-cool.

GB QTANi30Si5Cr5 Mechanical Properties

Temperature

0 - 30°C ≥ 300°C

PROPERTY / VALUE

Tensile Strength

≥ 390 MPa

Unlock full details

Brinell Hardness (HB)

170 — 250

Unlock full details

Elongation, A

val1 %

Unlock full details

Yield Strength, Rp0.2

val1 MPa

Unlock full details

Need complete mechanical properties to make the right choice?

Get complete data on strength, hardness, fatigue, and more.

Optimize material selection for your application - Book A Demo

Looking to compare materials and make better decisions?

Access reliable material data, compare options, and make better decisions faster.

With Total Materia, you can:

Compare materials based on real engineering data

Find equivalent materials across standards

Evaluate performance for your specific conditions

Check compliance with global regulations

See how this works for your specific application

Take a Guided Tour

72Cross References

16Composition
16Mechanical Properties
8Physical Properties
1Heat Treatment
-Metallography
-Machinability

-Stress-Strain
-Formability
-Fatigue
-Fracture
1Creep

-Joints
-Coatings
-Dimensions
-Tribology

4348Corrosion
-Ageing
-Weatherability
-Irradiation

-Total Suppliers