The production of high nitrogen steels produces several tough challenges which need to be overcome in order to achieve the associated benefits. Firstly, how to introduce the Nitrogen into the melt but also once it is present, how can it be kept in solid solution avoiding detriment to the finished product.

Since the beginning of their invention, the melting practices for High Nitrogen Steels, has two recognizable problems:

1. How to introduce high nitrogen contents into the melt;
2. How to keep nitrogen in solid solution during the process of solidification thus avoiding porosities in cast ingots.

To overcome these problems, nitrogen solubility evaluation models in the liquid state and solid state as well as different manufacturing routes were developed at the ETH Zurich.

Nitrogen can be added in many ways. It may come from molecular or ionised gas in the atmosphere at normal or elevated pressure or it may be offered by nitride ferro-alloys (FeCrN, FeMnN, FeVN, CrN, MnN) or highly concentrated ceramic nitrides (Si3N4).

Introduction may be made directly into the melt or indirectly through the slag [Feich99].

Figure 1 summarizes schematically, the alloy design for high nitrogen austenitic stainless steel produced without overpressure; an austenite free of porosities is achieved when the CrMnNi and eventually Mo contents are correctly balanced.

For these reasons ultrahigh strength austenitic stainless steel with high nitrogen amounts belong to the multicomponent system Fe-Cr-Mn-Ni-C-N, and they can be made with the following facilities:

  • Electroslag Remelting Furnace (ESR);
  • Induction or Electric Arc Furnaces, blowing N2 instead of Ar during the refining
  • Process in the Argon Oxygen Decarburisation (AOD) converter.

 

 



Figure 1: Schematic effect of main alloying elements used for high nitrogen austenitic stainless steels on austenite stability, pore formations and nitrogen solubility

 

Production of high nitrogen austenitic stainless steels by means of traditional steel making facilities, without overpressure, requires a balanced chemical composition of nitrogen solubility enhancer elements to prevent pore formation during the solidification.

Although many models for nitrogen solubility calculations exist in the literature of HNS, software like ThermoCalc are widely used among alloy developers, and they allow for empirical models for nitrogen solubility evaluation, based on analysis of a large number of experimental data. This may be very useful for a first estimation of the nitrogen content that might be expected on the base of the only chemical composition.

From a large number of high nitrogen austenitic steel grades developed at the ETH Zurich, the following model for nitrogen solubility was developed (alloying elements in weight percent):

 

N = 0.05 - Cr + 0.03 - Mn - 0.75 ...[ 1 ]

 

During this work many other high nitrogen austenitic stainless steels were melted, enriching the experimental databank for nitrogen solubility, and a new correlation was proposed fitting better the experimental data, as shown in Figure 2:

 

N = 0.066Cr + 0.02Mn + 0.19C - 0.025Ni + 0.05Mo - 1.05 ...[2]

 

17-78wt% Cr
0-30wt% Mn
0-49wt% Ni
0-7.3wt% Mo
0-0.3wt% C
0.3-1.5wt% N

 



Figure 2: Nitrogen solubility measured and calculated by equations [1] and [2] in austenitic stainless steels with chemical composition in the range

 

Equation [2] should be considered only as a rough estimation for nitrogen solubility as other important factors, like the temperature, are not included. Even with exclusion of these key variables a good fit within an error of about 15% was found.

November, 2012