High Strength Low Alloy V Steels: Part One

요약:

High-strength low-alloy (HSLA) steels, or microalloyed steels, are designed to provide better mechanical properties and/or greater resistance to atmospheric corrosion than conventional carbon steels.
Vanadium contributes to strengthening by forming fine precipitate particles (5 to 100 nm in diameter) of V(CN) in ferrite during cooling after hot rolling.

Low alloy steel is one of the most rapidly developed and highly utilized steel grades in recent years and has become the most produced, applied and economic steel available. The stipulated minimum yield strength is 275 MPa with a maximum value of 1035 MPa. A category of steel with these characteristics is made by adding a small proportion of alloy element in the carbon steel, which will ensure the steel has high strength, good toughness, high weldability and strong formality and erosion resistance under hot rolling or heat treatment conditions.

Normal elements for alloyment are generally strong carbide combination elements such as Ti, Nb and V. Nb are most widely applied and are the subject of most research projects due to the fact that it can effectively condition various physical metallurgy factors and have the biggest refinement and precipitation strengthening in traditional controlled rolling process. However, there has never been an equal determination to study the research and development of Ti-alloyed and V-alloyed microstructural steels.

High-strength low-alloy (HSLA) steels, or microalloyed steels, are designed to provide better mechanical properties and/or greater resistance to atmospheric corrosion than conventional carbon steels. They are not considered to be alloy steels in the normal sense because they are designed to meet specific mechanical properties rather than a chemical composition (HSLA steels have yield strengths greater than 275 MPa, or 40 ksi). The chemical composition of a specific HSLA steel may vary for different product thicknesses to meet mechanical property requirements.

The HSLA steels in sheet or plate form have low carbon content (0.05 to −0.25% C) in order to produce adequate formability and weldability, and they have manganese content up to 2.0%. Small quantities of chromium, nickel, molybdenum, copper, nitrogen, vanadium, niobium, titanium, and zirconium are used in various combinations.

Niobium and vanadium, the most frequently used micro alloy additives, are added to achieve similar objectives-to condition the austenite and to precipitate at various stages of processing. These two elements are not interchangeable however, and for optimum results, specific steel chemistry and processing parameters are required.

  Vanadium Niobium
Solubility of M (C,N) in austenite High Low
Propensity for Concast Cracking Low High
Ease of recrystalization High Low
Compatibility with Nitrogen Positive Negative
N effect on Precipitation in austenite Limited Intensive
N effect on Precipitation in ferrite Positive Absent
Nitrogen Binding Capacity Strong Minor

Table 1: Critical size of macro inclusions in cast semis that cause process upsets and product defects

High strength low alloy (HSLA) steels offer the advantage of weight and cost savings compared to mild steel. Therefore they are widely used in the automotive and the construction industry.

Vanadium Microalloyed Steels

The development of vanadium containing steels occurred shortly after the development of weathering steels, and flat-rolled products. With up to 0.10% V these materials are widely used in a hot-rolled condition. Vanadium-containing steels are also used in the controlled-rolled, normalized, or quenched and tempered condition.

Vanadium contributes to strengthening by forming fine precipitate particles (5 to 100 nm in diameter) of V(CN) in ferrite during cooling after hot rolling. These vanadium precipitates, which are not as stable as niobium precipitates, are in solution at all normal rolling temperatures and thus are very dependent on the cooling rate for their formation. Niobium precipitates, however, are stable at higher temperatures, which is beneficial for achieving fine-grain ferrite.

The austenite grain size of hot-rolled steels is determined by the recrystallization and grain growth of austenite during rolling. Vanadium hot-rolled steels usually undergo conventional rolling but are also produced by recrystallization controlled rolling. With conventional rolling, vanadium steels provide moderate precipitation strengthening and relatively little strengthening from grain refinement. The maximum yield strength of conventionally hot-rolled vanadium steels with 0.25% C and 0.08% V is about 450 MPa (65 ksi). The practical limit of yield strengths for hot-rolled vanadium-microalloyed steel is about 415 MPa (60 ksi), even when controlled rolling techniques are used.

Vanadium steels subjected to recrystallization controlled rolling require a titanium addition so that a fine precipitate of TiN is formed that restricts austenite grain growth after recrystallization. Yield strengths from conventional controlled rolling are limited to a practical limit of about 415 MPa (60 ksi) because of the lack of retardation of recrystallization. When both strength and impact toughness are important factors, controlled-rolled low-carbon niobium steel (such as X-60 hydrogen-induced cracking resistant plate) is preferable.

기술 자료 검색

검색할 어구를 입력하십시오:

검색 범위

본문
키워드

머릿글
요약

이 문서는 전체 문서 중 일부분입니다. 이 주제에 대해 더 읽고 싶으시면 아래 링크를 클릭하시면 됩니다.

화학 조성을 Total Materia 데이터베이스에서 검색하는 것은 매우 쉽습니다.

몇 초 내로 데이터베이스 내 175,000개 이상의 재질에서 유용한 화학 조성 데이터를 검색하는 것이 가능합니다.

신속 검색에 검색할 재질명을 입력합니다. 원하신다면 국가/규격을 지정하신 후 검색 버튼을 클릭합니다.


Total Materia 데이터베이스에서 검색된 관심 재질의 목록이 즉시 생성됩니다.
관심 재질을 클릭합니다.


소그룹 페이지에서, 선택된 재질의 화학 조성 링크를 클릭하여 데이터를 검토합니다. 화학 조성 데이터 기록의 개수는 링크 옆 괄호 안에 표시됩니다.


화학 조성 데이터는 참조를 위해 선택한 모든 재질 정보와 함께 표시됩니다.


Total Materia 데이터베이스를 사용해 보실 수 있는 기회가 있습니다. 저희는 Total Materia 무료 체험을 통해 150,000명 이상의 사용자가 이용하고 있는 커뮤니티로 귀하를 초대합니다.