The Aluminum Rolling Process: Part Two

Abstrakt:

There are numerous configurations of rolling mills including single stand mills and tandem stand mills.
One specific problem common to both configurations is related to the coating of the rolls which in turn can lead to surface quality issues on the finished strip. Countermeasures for this include the installation of brush rolls to maintain the cleanliness of the rollers.

The hot rolling operation is performed at the highest possible temperature to lower flow stress in order to reduce loads and to achieve high reductions. An upper temperature limit is imposed by the need for controlling recrystallization and precipitation, dependent on the alloy, as well as by the occurrence of pick-up. During conventional rolling, the coarse as cast structure changes to a deformed and recrystallized structure having a considerably finer grain size. Coarse primary precipitates are crushed and become distributed more evenly. Decreasing temperatures during rolling and an increase in vacancy concentration in the lattice due to deformation lead to a further precipitation of secondary phases.

With regards to microstructure, hot rolling can be seen as a succession of deformation and annealing steps. The most dominant metallurgical features are recrystallization and the development of preferred crystal orientations (texture). Both processes are interrelated and influenced by ongoing precipitation. Recrystallization is particularly determined by the alloy system and the processing conditions. In high purity aluminum, the grain boundary mobility is high and the material already shows rapid recrystallization during processing (dynamic recrystallization).

However, in customary industrial alloys, dynamic recrystallization may be observed only at extremely high temperatures, where the effect is mainly caused by local bulging of grain boundaries and not by nucleation and growth. For these materials, recrystallization typically takes place during inter-stand times or after rolling at elevated temperatures (post dynamic or static recrystallization). In commercially pure alloys such as AA1050, typically used for packaging foil or lithographic sheet, elements with low solubility, like Fe and Si, interact with grain boundaries and efficiently obstruct recrystallization when present as finely dispersed precipitates.

The presence of Mn and Cr causes the same effect unless the elements are already bound in coarse particles. Within the Al-Mg-Mn alloy system, used in considerable amounts for beverage cans or automotive components, recrystallization covers a broad range within the scope of industrial conditions and thus can be influenced to a large degree by the choice of rolling parameters. In industrial practice, the recrystallized structure can be obtained in a separate annealing treatment, but more sophisticated technologies utilize self-annealing on the coil from the rolling heat.

In a traditional hot mill, aluminum ingots are soaked in furnaces before they are brought to the Reversing or Break-Down Mill to be reduced to a long and slender strip. Once the strip is dramatically reduced, then it is passed on to the Finishing Mill, a series of rolls further down the same line, where it is further reduced to the final thickness before being coiled at the end of the process. A continuous rolling line casts a continuous thin slab, which progresses through a roughing mill, and then a finishing mill before being coiled, all in one, continuous process. A plate mill has one break down mill and a separate finishing mill. The plate is passes repeatedly under the same mill until the final thickness is obtained.

Figure 1 illustrates example configurations of aluminum hot rolling mills. The configuration of rolling mills varies depending on the intended amount of production. Singlestand mills are used for the production of wide variety products in small quantities, whereas tandem-stand mills are used for mass production. In recent years, a notably common practice has been to commence operation with single-stand mills in order to minimize initial investment and add rolling mills in line with rising demand to make the transition to tandem-stand mills.

Hot rolling mills for aluminum have roll coating problems, as aluminum powder sticking to the surface of the work rolls affects the surface quality of the rolled strips. Brush rolls and other special mechanisms are installed into aluminum rolling mills as countermeasures for such problems.



Figure 1: Typical arrangement of aluminum hot rolling mill

Durchforschen Sie bitte den Informationsteil der Datenbank

Geben Sie bitte eine Anfrage, um Suche einzuleiten:

Suche nach

Vollständiger Text
Schlüsselwörter

Überschriften
Abstracts

Die Total Materia Datenbank enthält mehrere tausende von Aluminiumwerkstoffe aus vielen Ländern und Normen.

Wenn zur Verfügung stehend, können alle Informationen über die Werkstoffeigenschaften angezeigt werden, einschliesslich chemische Zusammensetzung, mechanische und physikalische Eigenschaften, vortschrittliche Daten und vieles mehr.

Auf der Seite der erweiterten Suche, definieren Sie Ihre Kriterien indem Sie Aluminium aus der Liste der Werkstoffgruppen auswählen. Es kann auch notwendig sein daß Sie Ihre Suche weiter einschränken indem Sie die anderen Felder der erweiterten Suche, wie z.B. Land/Norm benutzen.

Klicken Sie auf "Absenden".


Es wird danach eine Liste von Werkstoffen angezeigt von welcher Sie auswählen können.


Nachdem Sie auf der Ergebnisliste auf den entsprechenden Werkstoff geklickt haben, wird eine Liste der Untergruppen, welche Normspezifikationen sind, angezeigt.

Von hieraus ist es möglich, spezifische Eigenschaften für den ausgewählten Werkstoff anzuzeigen und äquivalente Werkstoffe mit unseren leistungsstarken Cross-Reference Tabellen zu finden.


Klicken Sie auf den Link der Werkstoffdaten die Sie interessieren um diese anzuzeigen.




Um unsere Datenbank auszuprobieren, laden wir Sie ein sich unserer Nutzergemeinschaft von über 150 000 angemeldeten Benutzern, mit einem kostenlosen Probeaboanzuschliessen.